x3d auditory clear

Name: x3d auditory clear - Dentalcall
SKU: xc3-100-1-1-1-1-1-1-3-1-1-1-1
Availability: InStock

Favourite

use:

ITE Shells

In-Ear-Monitoring

Earmould Hearing Protection (active)

Hearing Protection (passive and solid)

Properties:

Initial transparency

High flexural & breaking strength

Very high construction precision,Very high surface hardness,No drying process required,Optimum depth curing,Brilliant clear

LC resin (wavelength 385 nm) for the 3D printing of earmoulds, InEar-Monitoring & ITE shells. Very high construction precision & surface hardness, maximum building speed. Brilliant transparency directly after printing process. Good mechanical flexural and breaking strength. No drying process required, long-term colour stable. Biocompatible,

Property	Unit measurement	Result
Hardness	Shore D	> 80
Flexural strength	MPa	> 75
Flexural modulus	MPa	> 1900
Tensile strength	MPa	> 50
Elongation		> 4 %

0 Sales

Other sellers:

psp —

SKU: xc3-100-1-1-1-1-1-1-3-1-1-1-1 Category: uncatagorized

UV curing premium resin (wavelength 385 nm) for generative manufacturing of hard ITE shells. Markedly lower viscosity than conventional materials (=> reduced loss of material, easier cleaning). Maximum construction safety, even for finest support structures, due to high initial hardness. Very high mechanical flexural strength and fracture resistance, without being brittle. Accelerated throughput by short light exposure times. Biocompatible & Bisphenol A free. Medical device Class IIa, standard colours: beige, black, white, intensive blue, intensive red

Property	Standard	Unit measurement	Result
Flexural strength	DIN EN ISO 178*	MPa	> 70
Flexural modulus	DIN EN ISO 178*	MPa	> 1800
Tensile strength	DIN EN ISO 527-1**	MPa	> 47
Elongation	DIN EN ISO 527-1**		> 9%
Hardness		Shore D	> 82