x3d auditory flex

Name: x3d auditory flex
SKU: xc3-100-1-1-1-1-1-1-3-1-1
Availability: InStock

use:

swimming plugs, hearing protection

Properties:

High initial hardness

Max building speed

Max construction precision with memory effect,Extremely impact resistant,high tear resistance,Fast elastic recovery

UV curing resin (wavelength 385 nm) for generative manufacturing of soft, massive earmoulds. High construction precision, maximum building speed. Highest transparency without fillers. High elastic recovery, good tear resistance, dimensional stable. With luxaprint® 3D flex printed earmoulds guarantee a natural wearing comfort: rigid at room temperature, flexible & smooth at body temperature. The earmould always returns to its original shape thanks to the material’s memory effect. luxaprint® flex coat for perfect surface finish. Biocompatible & Bisphenol A free. Medical device Class IIa. Colour: clear

Property	hardness	Result	Result
Hardness	Shore A	> 90 at room temperature	< 70 at body temperature
Tensile strength	MPa	> 8	> 8
Elongation		> 60 %	> 60 %
Tear strength	N/mm >	> 35 without luxaprint® flex coat	> 45 with luxaprint® flex coat

0 Sales

✅
Verified Seller

📦
Popular Item

🔒
Secure Order

📤
Share

Ask a Question

SKU: xc3-100-1-1-1-1-1-1-3-1-1 Category: uncatagorized

UV curing premium resin (wavelength 385 nm) for generative manufacturing of hard ITE shells. Markedly lower viscosity than conventional materials (=> reduced loss of material, easier cleaning). Maximum construction safety, even for finest support structures, due to high initial hardness. Very high mechanical flexural strength and fracture resistance, without being brittle. Accelerated throughput by short light exposure times. Biocompatible & Bisphenol A free. Medical device Class IIa, standard colours: beige, black, white, intensive blue, intensive red

Property	Standard	Unit measurement	Result
Flexural strength	DIN EN ISO 178*	MPa	> 70
Flexural modulus	DIN EN ISO 178*	MPa	> 1800
Tensile strength	DIN EN ISO 527-1**	MPa	> 47
Elongation	DIN EN ISO 527-1**		> 9%
Hardness		Shore D	> 82